PLA MATTE 3D Printing Filament 1.75mm 1Kg (Black) - ELEGOO

Matte surface finish

Experience the beauty of low saturation macaron colors with a matte finish. Unlike regular PLA, with a glossy or shiny surface, our PLA MATTE offers a matte texture that diffuses light and reduces visible lines between layers. Macaron colors add a touch of elegance and sophistication to your models, providing a soft look.

Exceptional Dimensional Accuracy

Our matte PLA stands out with an impressive dimensional accuracy of +/- 0.02mm and a tight tolerance of 1.75mm in diameter, ensuring consistency and precision in every print.

Eco-friendly Cardboard Coil

We understand the importance of sustainability. Therefore, all of our PLA mate is supplied on an eco-friendly card reel, which degrades faster than plastic reels. The coil has three viewing holes for easy monitoring of remaining filament and timely replacement.

High Compatibility

ELEGOO PLA MATTE filament is highly compatible with a wide range of FDM 3D printers available on the market. Works smoothly with various printer configurations and setups. Enjoy hassle-free printing with good reliability.

Improved Print Performance

Experience efficient and time-saving 3D printing with our PLA MATTE filament. Developed to reduce lint formation, warping, warping and shrinkage during printing, it ensures smoother, more accurate printed models with minimal distortions. With a print speed of up to 70mm/s, you can complete your creations quickly, enjoying a smooth, superior printing experience.

Specifications

Density: 1.31g/cm³
Melting index: 5-8(190°C/216kg)g/10min
Tensile strength (X-Y): = 42 MPa
Elongation at break (X-Y): 10%
Flexural strength: 80MPa
Flexural modulus: 2825MPa
Charpy impact resistance: 5.9 kj/m²
Thermal deformation temperature: 58°C(0.45MPa)
Fan: 100%
Line length (1.75mm): 330-340m
Recommended extrusion/nozzle temperature: 190~230°C (recommended 220°C)
Recommended heated bed temperature: 50-65°C
Printing speed: 30-70mm/s
Recommended platform: Textured paper, PVP glue, PEI